HALLSTAR DIOPLEX 195 is a low molecular weight polyester adipate. HALLSTAR DIOPLEX 195是一種低分子量聚酯的己二酸酯。 HALLSTAR DIOPLEX 195 is an excellent general-purpose plasticizer for both PVC and nitrile rubber. HALLSTAR DIOPLEX 195是一個(gè)的通用型增塑劑，PVC和橡膠。 HALLSTAR DIOPLEX 195 has a good combination of permanence to polar and non-polar mediums, which makes 195 well suited for general use plastisol applications. HALLSTAR DIOPLEX 195極性和非極性介質(zhì)，這使得195非常適合一般用塑料溶膠應(yīng)用具有持久性的良好結(jié)合。 HALLSTAR DIOPLEX 195 is also well suited for wire and cable applications because of its good electrical properties and physical properties. HALLSTAR DIOPLEX 195也非常適合用于電線和電纜應(yīng)用中，由于其良好的電性能和物理性能。
Many years of practical usage have established HALLSTAR DIOPLEX 195 as a good general purpose, polymeric plasticizer for both PVC and nitrile rubbers.多年的實(shí)際使用已經(jīng)建立了良好的通用高分子增塑劑用于PVC和橡膠。HALLSTAR DIOPLEX 195
|
|
Suggested Uses:使用建議：
Belts, Coated fabrics, Conveyor belts, Gaskets, General-purpose film, Hose and tubing, Industrial hose & tubing, Low viscosity plastisols, Oil seals, Phthalate alternative, Seals, and Wire & cable帶，涂層織物，輸送帶，密封墊，通用膜，軟管和管道，工業(yè)軟管，管材，低粘度塑料溶膠，油封，鄰二甲酸酯替代，密封件，電線電纜
Compatibility:兼容性：
Typical Properties:典型屬性：
|
Viscosity at 25°C, poises粘度在25℃時(shí)，泊
|
23 23
|
|
Viscosity at 25°C, cSt粘度在25℃，CST
|
2183 2183
|
|
Specific Gravity, 25°C比重，25°C
|
1.0925 1.0925
|
|
Refractive Index, 25°C折光率，25°C
|
1.4635 1.4635
|
|
Hydroxyl Value, mg KOH/g羥值，毫克KOH /克
|
25 25
|
|
Acid Value, mg KOH / g酸值，毫克KOH /克
|
1.4 1.4
|
|
Appearance外形
|
Pale yellow淡黃色
|
|
Odor, 25°C氣味，25°C
|
Slight sweet微甜
|
|
Flash Point, °F閃點(diǎn)，°F
Performance Properties:性能特性：
|
In PVC-EU歐盟在PVC-
|
|
Modulus, MN/m2 100％模量，MN/m2
|
8.3 8.3
|
|
Tensile Strength, MN/m2拉伸強(qiáng)度，MN/m2
|
17.3 17.3
|
|
Elongation at Break, %斷裂伸長率，％
|
390 390
|
|
Shore A Hardness邵爾A硬度
|
70 70
|
|
Tg, °C TG°C
|
-16 -16
|
|
Low Temperature Brittle Point, °C低溫脆化點(diǎn)℃
|
-14 -14
|
|
Low Temp Gehman T10,000 PSI, °C低溫格曼T10，000 PSI，°C
|
-14 -14
|
|
Volatilization揮發(fā)
|
-1.4 -1.4
|
|
Immersion/Extraction, Weight change, %浸入/提取，重量變化，％
|
|
|
Mineral Oil礦物油
|
-3.1 -3.1
|
|
Olive Oil橄欖油
|
-4.4 -4.4
|
|
Hexane正己烷
|
-2.5 -2.5
|
|
Distilled water蒸餾水
|
-0.9 -0.9
|
|
1% Soap Solution 1％的肥皂溶液
|
-7.6 -7.6
|
|
|
In PVC-US在PVC美
|
|
Shore A Hardness邵爾A硬度
|
70 70
|
|
Elongation at Break, %斷裂伸長率，％
|
390 390
|
|
Tensile Strength, MPa拉伸強(qiáng)度，MPa
|
17.3 17.3
|
|
Tensile Strength, psi拉伸強(qiáng)度，psi
|
2505 2505
|
|
Tg, °C TG°C
|
-16 -16
|
|
Low Temperature Brittle Point, °C低溫脆化點(diǎn)℃
|
-14 -14
|
|
Low Temp Gehman T10,000 PSI, °C低溫格曼T10，000 PSI，°C
|
-14 -14
|
|
Volatilization揮發(fā)
|
-1.4 -1.4
|
|
Immersion/Extraction, Weight change, %浸入/提取，重量變化，％
|
|
|
Hexane正己烷
|
-3.0 -3.0
|
|
1% Soap Solution 1％的肥皂溶液
|
-11 -11
|
|
Cottonseed Oil棉籽油
|
-4.9 -4.9
|
|
Distilled water蒸餾水
|
-1.2 -1.2
|
|
High humidity高濕度
|
-2.2 -2.2
|
|
Migration遷移
|
|
|
ABS ABS
|
Fair公平
|
|
Polystyrene聚乙烯
|
Exclnt EXCLNT
|
|
|
|
點(diǎn)擊圖片查看大圖