通用級 General Grade
|
ASTM
|
Unit
|
101-35
201-35 |
101-55
201-55 |
101-64
201-64 |
101-73
201-73 |
101-80
201-80 |
101-87
201-87 |
103-40
203-40 |
103-50
203-50 |
硬度Hardness 15s
5s |
2240
|
Shore
|
35A
40A |
55A
61A |
65A
69A |
73A
79A |
80A
86A |
87A
91A |
38D
42D |
48D
50D |
密度Density
|
D297
|
g/cm3
|
0.96
|
0.95
|
0.95
|
0.94
|
0.93
|
0.93
|
0.93
|
0.92
|
拉伸強度Tensile Strength
|
D412
|
MPa
|
3.5
|
5.2
|
7.0
|
8.6
|
10.8
|
14.2
|
22.5
|
26.5
|
定伸強度 Modulus
|
D412
|
MPa
|
1.1
|
2.0
|
2.4
|
3.5
|
4.9
|
6.8
|
11
|
13.5
|
伸長率Elongation
|
D412
|
%
|
300
|
350
|
400
|
400
|
420
|
450
|
560
|
580
|
撕裂強度Tear Strength
|
D624
|
KN/m
|
11
|
22
|
26
|
35
|
42
|
60
|
88
|
103
|
拉伸變形Tension Set
|
D412
|
%
|
4
|
5
|
6
|
10
|
15
|
20
|
30
|
50
|
壓縮變形Compression Set
(23°C,22h) (70°C,22h) (120°C,22h) |
D395
|
%
|
12
22 31 |
16
25 39 |
18
26 43 |
23
32 49 |
25
36 56 |
36
45 62 |
38
50 70 |
49
65 81 |
熱老化Heat Aging 150°C 168h
拉伸強度保持Tensile Strength Retain
|
% |
106 |
98 |
115 |
105 |
100 |
96 |
91 |
92 |
|
伸長率保持Elongation Retain
|
%
|
103
|
95
|
108
|
88
|
85
|
78
|
80
|
86
|
|
脆化溫度Brittle Temperature
|
D746
|
°C
|
-60
|
-60
|
-60
|
-60
|
-60
|
-50
|
-50
|
-40
|
阻燃級 Flame Retardant Grade
|
ASTM
|
Unit
|
151-60
251-60 |
151-70
251-70 |
151-80
251-80 |
151-90
251-90 |
153-40
253-40 |
153-50
253-50 |
Xl90
|
硬度Hardness 5s
|
2240
|
Shore
|
60A
|
70A
|
80A
|
90A
|
40D
|
50D
|
90A
|
密度Density
|
D297
|
g/cm3
|
1.1
|
1.1
|
1.1
|
1.1
|
1.1
|
1.1
|
1.5
|
拉伸強度Tensile Strength
|
D412
|
MPa
|
3.8
|
5.1
|
6.2
|
7.9
|
11
|
13
|
6.8
|
伸長率Elongation
|
D412
|
%
|
450
|
340
|
250
|
240
|
210
|
200
|
190
|
撕裂強度Tear Strength
|
D624
|
KN/m
|
19
|
25
|
32
|
45
|
58
|
71
|
28
|
阻燃等級3mm
|
UL-94
|
V-0
|
V-0
|
V-0
|
V-0
|
V-0
|
V-0
|
V-0
|
|
脆化溫度Brittle Temperature
|
D746
|
°C
|
-60
|
-58
|
-57
|
-55
|
-50
|
-40
|
-50
|
加工指南:
·1. 預干燥 80 ~ 90℃ 2~4小時
·2. 用PP 或 PE清洗料筒
·3. 使用基于PP 或 PE 的色母
·4. 注塑溫度 190℃ ~ 250℃注塑壓力 40 ~ 60 MPa
·5. 擠塑溫度 170℃ ~ 230℃口模成型段 < 10 mm 濾網(wǎng) 60 ~100目